ASTM A556/A556M Feedwater Heater Tubes

ASTM A556/A556M Standard Specification for Seamless Cold-Drawn Carbon Steel Feedwater Heater Tubes

1. ASTM A556/A556M Scope

1.1 This specification 2 covers minimum-wall-thickness, seamless cold-drawn carbon steel tubes including bending into the form of U-tubes, if specified, for use in tubular feedwater heaters.

1.2 The tubing sizes covered shall be 5/8 to 1 1/4 -in. [15.9 to 31.8-mm] outside diameter, inclusive, with minimum wall thicknesses equal to or greater than 0.045 in. [1.1 mm].

1.3 Optional supplementary requirements are provided, and when desired, shall be stated in the order.

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently ofthe other. Combining values from the two systems may result in nonconformance with the specification. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.

2. ASTM A556/A556M Referenced Documents

2.1 ASTM Standards:

A 450/A 450M Specification for General Requirements for Carbon, Ferritic Alloy, and Austenitic Alloy Steel Tubes

E 30 Test Methods for Chemical Analysis of Steel, Cast Iron, Open-Hearth Iron, and Wrought Iron

ASTM A556 Feedwater Heater Tubes3. ASTM A556/A556M Ordering Information

3.1 Orders for material under this specification should include the following as required to describe the desired material adequately:

3.1.1 Quantity (feet, metres, or number of pieces),

3.1.2 Name of material (seamless steel tubing),

3.1.3 Dimensions (outside diameter and minimum wall thickness),

3.1.4 Length (specific or random),

3.1.5 Manufacture (cold drawn),

3.1.6 Grade (chemical composition),

3.1.7 Optional requirements,

3.1.8 Bending Requirements— If order specifies tubes to be bent, the design of the U-tubes shall accompany the order. Purchaser must specify if stress-relief anneal of the U-bends is required,

3.1.9 Test report required (see Certification Section of Specification A 450/A 450M),

3.1.10 Specification number, and

3.1.11 Special requirements and any supplementary requirements selected.

4. ASTM A556/A556M General Requirements

4.1 Material furnished to this specification shall conform to the applicable requirements of the current edition of the Specification A 450/A 450M, unless otherwise provided herein.

5. ASTM A556/A556M Manufacture

5.1 Manufacture—Tubes shall be made by the seamless process and shall be cold drawn.

5.2 Heat Treatment:

5.2.1 Cold-drawn tubes shall be heat treated after the final cold-draw pass at a temperature of1200°F [640°C] or higher to ensure ductility satisfactory for rolling into tube sheets and to meet mechanical properties as specified.

5.2.2 If stress-relief anneal of the U-bends is specified, the anneal shall consist of heating the bent portion within a range of 1100 to 1200°F [585 to 640°C].

6. ASTM A556/A556M Chemical Composition

6.1 The steel shall conform to one of the requirements as to chemical composition as prescribed in Table 1.

6.2 When a grade is ordered under this specification, supplying an alloy grade that specifically requires the addition of any element other than those listed for the ordered grade in Table 1 is not permitted.

7. ASTM A556/A556M Product Analysis

7.1 When requested in the purchase order, a product analysis shall be made by the manufacturer or supplier from one tube or billet per heat.

7.2 If the original test for product analysis fails, retests of two additional tubes or billets shall be made. Both retests for the elements in question shall meet the requirements of this specification; otherwise, all remaining material in the heat or lot (Note 1) shall be rejected or, at the option of the producer, each tube may be individually tested for acceptance. Tubes that do not meet the requirements of this specification shall be rejected.

N OTE 1—For tension and hardness test requirements, the term lot applies to all tubes prior to cutting, ofthe same nominal diameter and wall thickness which are produced from the same heat ofsteel. When final heat treatment is in a batch-type furnace, a lot shall include only those tubes of the same size and the same heat which are heat treated in the same furnace charge. When the final heat treatment is in a continuous furnace, a lot shall include all tubes ofthe same size and heat, heat treated in the same furnace at the same temperature, time at heat and furnace speed.

7.3 For referee purposes, Test Methods E 30 shall be used.

ASTM A556 Chemical Requirements

8. ASTM A556/A556M Mechanical Properties

8.1 Tensile Properties—The material shall conform to the requirements as to tensile properties prescribed in Table 2, when pulled in full section.

8.2 Hardness Requirements—The tubes shall not exceed the Rockwell Hardness shown in Table 3.

ASTM A556 Tensile Requirements9. ASTM A556/A556M Permissible Variations in Dimensions (Fig. 1)

9.1 Permissible variations from the specified outside diameter shall not exceed 60.004 in. [0.10 mm] for tubing under

1.0-in. [25.4-mm] outside diameter nor 60.006 in. [0.15 mm] for tubing 1.0 in. [25.4 mm] to 1.25 in. [31.7 mm] inclusive. These tolerances do not apply to the bent portion of the U-tubes. At the bent portion of a U-tube for R = 2 3 D or greater neither the major nor minor diameter of tube shall deviate from nominal by more than 10 %. If 1 1 ⁄ 2 D is specified, tolerances could be greater.

9.2 Permissible variations from the specified minimum wall thickness shall not exceed +20 % or −0. The wall thickness of the tube in U-bent section shall be not less than value

determined by: t f 5 T ~ 2R ! / ~ 2R1D ! (1) where:

t f = wall thickness after bending, in. [mm],

T = specified minimum tube wall thickness, in. [mm],

R = centerline bend radius, in. [mm], and

D = nominal outside tube diameter, in. [mm].

9.3 In the case of U-tubes, the length of the tube legs as measured from the point of tangency of the bend and the tube leg to the end ofthe tube leg shall not be less than specified, but may exceed the specified values by the amount given in Table

4. The difference in lengths of the tube legs shall not be greater than 1/8 in. [3 mm] unless otherwise specified.

9.4 The end of any tube may depart from square by not more than the amount given in Table 5.

9.5 The leg spacing measured between the points of tangency of the bend to the legs shall not vary from the value (2R− specified tube OD) by more than 1/16 in. [1.5 mm] where R is the centerline bend radius.

9.6 The bent portion of the U-tube shall be substantially uniform in curvature and not exceed 6 1/16 in. [61.5 mm] ofthe normal centerline radius.

10. ASTM A556/A556M Workmanship, Finish, and Appearance

10.1 Finished tubes shall be free from scale but may have a superficial oxide film on the surfaces. Alight oxide scale on the outside and inside surfaces of U-bend shall be allowed for tubes which have been heat treated.

10.2 Finished tubes shall be reasonably straight and have smooth ends free from burrs. Tubes shall have a workmanlike finish and shall be free of surface imperfections that cannot be removed within the allowable wall tolerances. Removal of surface imperfections such as handling marks, straightening marks, light mandrel and die marks, shallow pits, and scale pattern will not be required provided they are within the allowable wall tolerances.

10.3 Finished tubes shall be coated both on the outside and the inside diameter to prevent corrosion in transit. The type of coating applied should be mutually agreed upon and specified in the order.

11. ASTM A556/A556M Mechanical Tests Required

11.1 Tension Test—One tension test shall be made on a specimen for lots of not more than 50 tubes. Tension tests shall be made on specimens from two tubes for lots of more than 50 tubes (Note 1).

11.2 Flattening Test—One flattening test shall be made on specimens taken from each end of one finished tube, not the one used for the flaring test, from each lot ofnot more than 125 tubes or fraction thereof.

11.3 Flaring Test—One flaring test shall be made on specimens taken from each end of one finished tube, not the one used for flattening test, from each lot of not more than 125 tubes or fraction thereof.

11.4 Hardness Test—Brinell or Rockwell hardness tests shall be made on specimens from two tubes from each lot (Note 1).

11.5 Hydrostatic Test—Each U-tube shall be subjected to a hydrostatic test, using a noncorrosive fluid, or when agreed upon between the purchaser and manufacturer, they may be tested at 1 1 ⁄ 2 times the specified design working pressure.

12. ASTM A556/A556M Nondestructive Test (Electric Test)

12.1 Each tube shall be tested after the finish heat treatment following the final cold-drawn pass by passing through a nondestructive tester capable of detecting defects on the entire cross section of the tube, in accordance with Specification A 450/A 450M.

13. ASTM A556/A556M Packaging and Package Marking

13.1 The tubing shall be packaged or bundled in such a manner as to prevent damage in ordinary handling and transportation and identified by a tag with the name of the manufacturer, purchase order number, specification number and grade, and size.

13.2 In the case of U-tubes, each box shall be palletized and legibly marked showing the manufacturer’s name, purchase order number, specification number and grade, size, and identification of items contained.

13.3 Bar Coding—In addition to the requirements in 13.1 and 13.2, bar coding is acceptable as a supplemental identification method. The purchaser may specify in the order a specific bar coding system to be used.

14. ASTM A556/A556M Keywords

  ASTM A556 Feedwater Heater Tubes|Carbon Steel Feedwater Heater Tubes|U Bend ASTM A556 Feedwater Heater   Tubes

Comments

Post a Comment

Popular posts from this blog

What is tube sheet layout?

What is tube sheet layout? A tube sheet is a component used in shell and tube heat exchangers and other types of heat transfer equipment. It is a flat plate with holes drilled in it, through which tubes are inserted and secured. The tube sheet serves as a barrier between the two fluids, allowing heat to be transferred from one to the other. The layout of the tube sheet depends on the design of the heat exchanger, which includes the number of tubes, the size of the tubes, and the spacing between the tubes. The layout is typically determined using computer-aided design (CAD) software, which can optimize the placement of the tubes to achieve the desired heat transfer performance. In general, the tubes are arranged in a triangular or square pattern on the tube sheet. The triangular pattern is often preferred because it provides better support for the tubes and reduces the risk of vibration and damage. The spacing between the tubes is also important, as it affects the flow rate and pressure...
Post a Comment
Read more

What is aluminum finned tubes?

What is aluminum finned tubes? Aluminum finned tubes are a type of finned tube air heat exchanger that uses aluminum fins attached to a tube made of a different material, such as copper or steel. The aluminum fins are typically extruded or formed to increase the surface area of the tube, which in turn increases the efficiency of heat transfer. Aluminum finned tubes are commonly used in HVAC systems, as well as in industrial and power plant applications. They are preferred over other types of finned tubes in some applications because they are lightweight, corrosion-resistant, and have good thermal conductivity. Additionally, aluminum is relatively inexpensive compared to other metals commonly used in heat exchangers, such as copper and stainless steel. The specific properties of aluminum finned tubes can vary depending on the alloy used to make the fins. For example, aluminum fins made from alloys such as 6061 and 3003 have good corrosion resistance and thermal conductivity, while those...
Post a Comment
Read more

What is the difference between pipe bends and elbows?

Bends and elbows are fittings used to change the direction of a pipe. These two kinds of pipe fittings have a wide range of applications in construction, but in actual use, the performance of pipe bends and elbows is different, and elbows are used much more than pipe bends. What is the difference between pipe bends and elbows? An elbow is a pipe part with a bend, which is a commonly used pipe part. Bends are usually manufactured to specific needs. Compared with the elbow, the elbow is much longer and is a curved pipe, while the elbow is only a part that changes the direction of the pipe. Although both are components that change the direction of the pipeline, there are many differences between these two components. 1. Different manufacturing processes for  pipe bends and elbows In the manufacturing process cold and hot bent pipes can be made of pipe bends, which directly bent by the pipe bending machine, and the  bent pipe  can be manufactured at one time without secondary...